烨辉镀锌、镀铝锌制程介绍

一、前处理及退火

采用最新式非氧化性直火燃烧炉 (Non-Oxidizing Direct Flame Furnace)先将原板(冷轧或热轧酸洗钢板)表面之残油除去,再进入退火炉,加热至再结晶温度以上,使钢板软化,以利用户之成形加工。

Pre-treatment  and Annealing Residual oil on the surface of the cold rolled or pickled strip is cleaned off in the non-oxidizing direct fl ame furnace (NOF). The strip is then softened through recrystallization in the annealing furnace.

 

二、锌花调整

钢带离开镀槽,以空气刀控制镀层量后再以锌粉吹射尚未固化之锌层或以微细化水雾喷射锌层,或控制镀槽成分 组成,均可得微细锌花或无锌花表面。

Mini Spangle Device The thickness of  the coating layer is precisely controlled by the air knife. Zinc powder or atomized fog are blown on to the coating layer before it solidifies to produce minimized (zero) spangles. Another way to produce minimized (zero) spangles is through control of the metal pot composition mixture in the galvanizing pot.

 

三、调质与整平

高性能之调质机及张力整平机,可改善镀层表面之均匀性及板形,提高产品质量。

Skinpass and Tension Levelling This process ensures the fl atness of the strip and improves the surface uniformity.

 

四、表面处理

于镀层之表面施予铬酸化成处理或 涂覆有机树脂 ( 耐指纹涂膜 ) 处理,以减少或避免在储存、使用时白锈之产生。

Surface Treatment The surface of the coated strip is treated with chromic acid or organic resin (anti-fi ngerprint) to minimize the occurrence of white rust.

 

五、镀锌/镀铝锌制程

镀槽内添加铝 (Al),抑制脆硬之锌 铁合金层的形成,可得成形性优越,附着性良好之热浸镀锌钢板。此产品命名为「美利新镀锌钢板 (PhuizerZinc)」。 本公司亦可生产镀 5% 铝锌及镀 55% 铝锌钢板,主要系在此制程之改变。 镀 5% 铝锌钢板产品名称为「铝锌 凤 (PhuizerFan)」,因含有微量之镧铈合金成分可以改善钢板镀层之湿润性, 提供绝佳之成形性与冲压性,优良之涂装性及良好的熔接性。 镀 55% 铝锌钢板产品名称为「铝 锌龙 (PhuizerLume)」,镀层铝含量约 55%、硅含量约 1.5 %,具有优良之抗腐蚀性、抗高温氧化性和热反射性及良好的涂装性。

Coating This strip is coated by dipping into a pot of molten zinc. The aluminum is added to the pot and precisely controlled to avoid a brittle Zn-Fe alloy layer. This product's name is 'PhuizerZinc'. When the coating material replaced with a 5% Al-Zn composition, the coated steel product is called 'PhuizerFan'. The composition of mischmetals in the pot improves the wettability and offers extraordinary formability, drawability, excellent paintability and good weldability. When the coating  material  replaced  with  a  55%  Al-Zn composition, the coated steel product is called 'PhuizerLume'. Both laboratory and long-term outdoor exposure tests showed that the alloy coating gives optimum corrosion resistance, high temperature oxidation resistance and good paintability. The coated alloy is composed of about 55% aluminum, 1.5% silicon and balanced zinc, by weight.

烨辉镀锌、镀铝锌制程介绍 

久复企业涉足涂镀钢板行业近十余年,主要从事涂镀钢板贸易,拥有多年丰富经验。公司拥有优秀团队,有需要订购宝钢、马钢、首钢、烨辉彩涂钢板、镀锌板、镀铝锌板的朋友们,我们欢迎您的咨询、订购、以及参观!或拨打电话:

李经理:13641778586


News / 推荐新闻 More
2020 - 02 - 26
点击次数: 88
针对疫情对钢铁行业的影响,骆铁军表示,疫情对钢铁行业的影响集中在六个方面:一是交通运输受限,原辅料供应紧张,产品出库困难。二是下游需求下降。三是春节后钢材库存增加较快。四是出口可能受影响。五是钢材价格下跌,铁矿石价格上涨。六是钢铁企业实施减产措施。中钢协:高库存致钢铁业资金紧张 多策略缓解债务风险受疫情影响,企业资金回笼难度加大。但当前会员钢铁企业资产负债率为63.16%,同比下降1.34个百分点,连年下降,总体处于健康水平。受成本上升、钢价下跌的影响,钢铁企业实现利润会有所下降,资金压力也会有所加大。将采取多渠道筹措资金、加强内部管理,提高资金使用效率、减少非必要支出、控制生产节奏等措施缓解资金压力,防范资金风险。陕晋川甘论坛钢企协同减产比例提高到35%。为积极响应中国钢铁工业协会《凝心聚力,共克时艰,共同维护钢铁行业平稳健康发展》的倡议,减少疫情对钢铁行业产生的影响,陕晋川甘论坛加强协...
2020 - 02 - 26
点击次数: 230
随着市场的不断变化,烨辉在2019年就开始着手调整镀槽锌液的成份,在2020年一月调整完毕备便,待复工后试制。在2020年2月18日,烨辉成功产出第一卷锌铝镁钢卷。烨辉于2011年量产--锌铝镁(低镁)的产品,后又把镁含量再度提高,使产品耐蚀性能、成型性能有显著的提升,但同时镁含量的提高也会大大的提升生产的难度。张副董事长兼总经理 永芳与镀锌一课第一卷锌铝镁产品合影1. 作为彩涂卷的基材,可以延长产品的使用寿命(正常使用20年以上)2.镀制品用途3.产品运用
2020 - 02 - 25
点击次数: 352
1、彩涂钢板的生产工艺彩涂钢板的生产工艺很多,但是目前用的最多的是传统的辊涂+烘烤工艺,由于建筑用涂层道次以2涂为多,因此,传统的2涂2烘是最典型的彩涂钢板生产工艺,彩涂机组的主要工艺包括预处理工艺、涂敷工艺、烘烤工艺。简单的工艺流程包括:开卷—缝合—脱脂—化学预处理—初涂—初涂烘烤—初涂冷却—精涂—精涂烘烤—精涂冷却—检查—分剪—卷取。典型彩涂钢板生产工艺图(1)预处理工艺钢卷经脱脂、水洗后,在经过磷化或者复合氧化,在钢板表面形成一层磷酸盐或者复合氧化物膜,再经过钝化封闭处理,形成的预处理膜是提高基板和涂料之间附着力的有效手段。(2)涂敷工艺彩涂机组一般采用辊涂方式将涂料涂敷在带钢表面。辊涂是在辊子上先形成一定厚度的膜,然后再将这层涂料转移到带钢表面的涂装方法。它适用于平板或带钢的涂层,速度快,生产效率高,不产生涂雾,涂布效率接近100%,仅在清洗涂层机时产生少量废溶剂;靠调节辊子间隙、...
Copyright ©2018 - 2021 久复(上海)国际贸易有限公司