烨辉镀锌、镀铝锌制程介绍

日期: 2019-08-26
浏览次数: 120

烨辉镀锌、镀铝锌制程介绍

一、前处理及退火

采用最新式非氧化性直火燃烧炉 (Non-Oxidizing Direct Flame Furnace)先将原板(冷轧或热轧酸洗钢板)表面之残油除去,再进入退火炉,加热至再结晶温度以上,使钢板软化,以利用户之成形加工。

Pre-treatment  and Annealing Residual oil on the surface of the cold rolled or pickled strip is cleaned off in the non-oxidizing direct fl ame furnace (NOF). The strip is then softened through recrystallization in the annealing furnace.

 

二、锌花调整

钢带离开镀槽,以空气刀控制镀层量后再以锌粉吹射尚未固化之锌层或以微细化水雾喷射锌层,或控制镀槽成分 组成,均可得微细锌花或无锌花表面。

Mini Spangle Device The thickness of  the coating layer is precisely controlled by the air knife. Zinc powder or atomized fog are blown on to the coating layer before it solidifies to produce minimized (zero) spangles. Another way to produce minimized (zero) spangles is through control of the metal pot composition mixture in the galvanizing pot.

 

三、调质与整平

高性能之调质机及张力整平机,可改善镀层表面之均匀性及板形,提高产品质量。

Skinpass and Tension Levelling This process ensures the fl atness of the strip and improves the surface uniformity.

 

四、表面处理

于镀层之表面施予铬酸化成处理或 涂覆有机树脂 ( 耐指纹涂膜 ) 处理,以减少或避免在储存、使用时白锈之产生。

Surface Treatment The surface of the coated strip is treated with chromic acid or organic resin (anti-fi ngerprint) to minimize the occurrence of white rust.

 

五、镀锌/镀铝锌制程

镀槽内添加铝 (Al),抑制脆硬之锌 铁合金层的形成,可得成形性优越,附着性良好之热浸镀锌钢板。此产品命名为「美利新镀锌钢板 (PhuizerZinc)」。 本公司亦可生产镀 5% 铝锌及镀 55% 铝锌钢板,主要系在此制程之改变。 镀 5% 铝锌钢板产品名称为「铝锌 凤 (PhuizerFan)」,因含有微量之镧铈合金成分可以改善钢板镀层之湿润性, 提供绝佳之成形性与冲压性,优良之涂装性及良好的熔接性。 镀 55% 铝锌钢板产品名称为「铝 锌龙 (PhuizerLume)」,镀层铝含量约 55%、硅含量约 1.5 %,具有优良之抗腐蚀性、抗高温氧化性和热反射性及良好的涂装性。

Coating This strip is coated by dipping into a pot of molten zinc. The aluminum is added to the pot and precisely controlled to avoid a brittle Zn-Fe alloy layer. This product's name is 'PhuizerZinc'. When the coating material replaced with a 5% Al-Zn composition, the coated steel product is called 'PhuizerFan'. The composition of mischmetals in the pot improves the wettability and offers extraordinary formability, drawability, excellent paintability and good weldability. When the coating  material  replaced  with  a  55%  Al-Zn composition, the coated steel product is called 'PhuizerLume'. Both laboratory and long-term outdoor exposure tests showed that the alloy coating gives optimum corrosion resistance, high temperature oxidation resistance and good paintability. The coated alloy is composed of about 55% aluminum, 1.5% silicon and balanced zinc, by weight.

烨辉镀锌、镀铝锌制程介绍 

久复企业涉足涂镀钢板行业近十余年,主要从事涂镀钢板贸易,拥有多年丰富经验。公司拥有优秀团队,有需要订购宝钢、马钢、首钢、烨辉彩涂钢板、镀锌板、镀铝锌板的朋友们,我们欢迎您的咨询、订购、以及参观!或拨打电话:

李经理:13641778586


News / 推荐新闻 More
2020 - 07 - 10
点击次数: 23
新热镀锌国家标准GB/T 2518-2019综合考虑了汽车、家电、建筑行业等用户需求,以高质量具有引领性为导向,以EN、JIS、ASTM、SAE、JFS等国外先进标准和行业协会标准为参考,在大量调研和对国内外标准资料分析研究基础上,并广泛征求国内各大钢厂、用户、研究院所的意见,并以此为基础完成升级改版。新的国家标准对钢种设置进行了系列化,最高强度拓展至1200MPa,更好支撑汽车工业的轻量化;并引入了更多的环保的、特殊要求的后处理方式,更好地引领热镀锌行业走“高强、绿色、环保”之路,促进先进生产力与汽车板、家电板等高等级、高附加值的产品需求匹配对接。热镀锌钢板是一种具有优良耐蚀性的钢材,也是冷轧涂镀层板中用途最广、产量最大的产品,广泛应用于国民经济的各个领域如汽车、家电、建筑等行业,与民众的日常生活息息相关。☆1连续热镀锌国家标准GB/T 2518的变迁历史中国热镀锌国家标准自1981年以...
2020 - 07 - 08
点击次数: 46
如何选择耐指纹板的膜厚?1 耐指纹板导电性能与膜厚的关系为了防止部分家电电磁波噪音的泄漏,组装后部件必须接地,这就要求钢板有较好的导电性。耐腐蚀性与膜厚成正比,而导电性与膜厚成反比,这是一对矛盾,达到耐蚀性和导电性的统一,就必须将膜厚控制在最佳范围内。耐指纹膜厚对耐腐蚀性能和导电性能影响的曲线如下图所示。图中的蓝线说明钢板产生白绣的百分比随着耐指纹膜厚急剧下降,当膜厚达到1.0 g/m2时,基本就不会发生白绣。图中红线说明钢板表面电阻OL率比随着耐指纹膜厚急剧上升,当膜厚超过1.5 g/m2时,对导电性带来很大的影响。因此,只有当耐指纹膜厚控制在1.0-1.5g/m2时,才能做到耐腐蚀性和导电性的统一,这一工艺窗口很窄,对工艺控制的要求非常高。2 综合选择耐指纹板膜厚为了综合考虑导电性、耐腐蚀性和耐高温黄变性,选择最佳膜厚,进行了实际试验,结果如下表所示。表在不同粗糙度...
2020 - 07 - 08
点击次数: 60
彩涂卷表面划伤问题基础知识介绍◇1、概述彩涂板在生产、搬运和使用过程中难免磕碰,造成产品的破损,影响正常使用。为了保障产品的正常使用,这里简单讲下彩涂板表面划伤问题的原因和解决方法。表面划伤是彩涂板生产时产品表面缺陷的一种, 它不但影响了彩涂产品的外观,而且会使划伤彩涂产品的抗腐蚀性降低。它按来源可分为原料划伤和生产工序划伤。 ◇2、原料表面划伤原料表面划伤是指基板在镀锌生产时就产生的质量缺陷。使用带有划伤的基板生产彩涂板时易使生产出来的彩涂板 表面产生色差甚至漏涂的质量缺陷。具体解决方法:控制措施为检查上工序中的生产质量,防止带有划伤的原料基板入厂。◇3、生产过程产生的划伤1.入、出口导导板表面有异物板划伤,缺陷部位位于钢板背面,造成问题的主要原因为导板表面有异物。具体解决方法:定期检查导板磨损情况,进行修复、调整;及时将松动的导板螺钉进行加固,及时清除导板表面异物。 ...
Copyright ©2018 - 2021 久复(上海)国际贸易有限公司